Polyol ISO for marine fender shock absorption mat
- Min. Order:
- 1000 Kilogram
- Min. Order:
- 1000 Kilogram
- Transportation:
- Ocean, Land, Air
- Port:
- Shanghai
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | China |
|---|---|
| Productivity: | 250000 tons/year |
| Supply Ability: | 250000 tons/year |
| Payment Type: | L/C,T/T |
| Incoterm: | FOB,CIF |
| Transportation: | Ocean,Land,Air |
| Port: | Shanghai |
XC-1065N/XC-5009
Polyurethane Raw Materials
Characteristic:Good hydrolysis resistance and high strength
Application:Marine fender,shock absorption mat and polyether outsole
Typical properties of PU matrix
Name of products
Appearance
Viscosity(mPa.s/40℃)
Density(g.cm-3/40℃)
XC-1065N
cream white liquid
400-800
1.01-1.02
XC-5009
Yellowish transparent liquid
300-600
1.08-1.2
Materials preheat
XC-1065N:preheated at 50-60℃ for 2-4 hours
XC-5009:preheated at 60-70℃ for 8-10 hours
Shoe Sole Pu Chemical
Typical processing parameters & Reaction parameter
Items
A/B Materials Temperatures(℃)
Mix ratio (By the weight)
Cream Time(s)
End of Rise Time(s)
Free Rise Foam Density(g/cm3)
Mold Temperature(℃)
Demold Time(min)
Parameter
30-35/35-40
100/108-110
8-10
60-70
0.25-0.35
35-45
7-9
Physical properties
Shock Absorption Mat Raw Materials
Physical properties
Molded Density(g/cm3)
Hardness(Shore C)
Tensile strength(Mpa)
Elongation(%)
Tear Strength(kN/m)
DIN abrasion(mm3)
Hydrolysis
Physical properties
0.50-0.70
65-80
3.5-5.5
380-450
17-22
270-350
＞95
Demold time may be prolonged with the increase of sole thickness
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference.The detail data are subjected to practical production.If other requests for physical properties,please contact us.