marine fender and sole material Casting polyurethane resins
- Min. Order:
- 1000 Kilogram
- Min. Order:
- 1000 Kilogram
- Transportation:
- Ocean, Land, Air
- Port:
- Shanghai
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | China |
|---|---|
| Productivity: | 260000tons/month |
| Supply Ability: | 250000 tons/year |
| Payment Type: | L/C,T/T |
| Incoterm: | FOB,CIF |
| Transportation: | Ocean,Land,Air |
| Port: | Shanghai |
Pu For Shock Absorber
Characteristic:Good handle, hydrolysis resistance and cold resistance, high elasticity
Application: Cold resistance sole, marine fender, shock absorption mat
Marine Fender Pu Chemical
Typical properties of PU matrix
| Name of products | Appearance |
Viscoscity (mPa·s/40℃) |
Density (g·cm-³/40℃) |
Package (kg) |
| A-7150 | Liqud | 1000-1400 | 1.01-1.02 | 18 |
| B-8260 | Yellowish Transparent liquid or waxy | 700-1100 | 1.08-1.2 | 20 |
Materials preheat
A-7150: preheated at 50-60℃ for 6-8 hours
B-8260: preheated at 50-60℃ for 8-12 hours
Typical processing parameters & Reaction parameter
| Items | A/B Materials Temperatures(℃) |
Mix ratio A+C/B (By weight)
|
Cream time (s) |
End of Rise Time (s) |
Free Rise Foam Density (g/cm³) |
Mold Temperature (℃) |
Demold Time (min) |
| Parameter | 40-45/38-42 | 100/94-95 | 9-11 | 60-70 | 0.25-0.30 | 45-55 | 5-7 |
The adding content of C-2 should be 240g±10g/18kg
The adding content of water should be 0-40g/18kg according to the reality
Shoes Making Material
Physical properties
| Items |
Molded Density (g/cm³)
|
Hardness (Shore A)
|
Tensile strength (Mpa)
|
Elongation (%)
|
Tear strength (kN/m) |
DIN abrasion (mm³) |
Flexing resistance (Break length 4mm)(-20℃) |
|
Physical properties
|
0.55-0.70 | 55-70 | 8.0-13.5 | 500-750 | 38-50 | 60-100 | 40000 times no increasing |
Demold time may be prolonged with the increse of sole thickness
These physical data are acquired by testing a sample of 6mm thick
Data listed above are just for reference.The data are subjected to practical production.If other requests for physical properties,please contact us.