Polyurethane Raw Materials
PU for sole low density high flexing resistance
Characteristic: medium-hardness, transparent material
Application: For transparent shoes sole
Typical properties of PU matrix
|
Shoe Sole Pu Chemical Materials preheat XC-6680: preheated at 50-60℃ for 8-10 hours XC-8260: preheated at 50-60℃ for 8-12 hours The adding content of C-2 should be 220g±10g/18kg
|
|
Items |
A/B Materials Temperatures (℃) |
A+C/B Mix ratio (By weight) |
Cream Time (s) |
Free Rise Foam Density (g/cm3) |
Mold Temperature (℃) |
Demold Time (min) |
|
Parameter |
40~45/40~45 |
100/51 |
- |
0.9~1.2 |
45~55 |
6~8 |
|
Items |
Molded Density (g/cm3) |
Hardness (Shore A ) |
Tensile strength (MPa) |
Elongation (%) |
Tear Strength (kN/m) |
Flexing resistance ( Break length, 4mm) |
Williams abrasion (cc/php)
|
|
Physical properties |
0.9~1.2 |
55~65 |
10~14 |
550~650 |
40~55 |
No crack |
60~100 |
Demold time may be prolonged with the increse of sole thickness
These physical data are acquired by testing a sample of 6mm thick
Data listed above are just for reference.The data are subjected to practical production.If other requests for physical properties,please contact us.