Safety Shoe System
Characteristic:High strength and cohesive force, good abrasion resistance
Application: Double density sole system for common safety shoes and one-step forming casual shoes, outsole
Typical properties of PU matrix
| Name of products | Appearance |
Viscoscity (mPa·s/40℃) |
Density (g·cm-³/40℃) |
Package (kg) |
| A-6170 | liquid | 1000-1400 | 1.01-1.02 | 18 |
| B-8280 | Yellowish Transparent liquid or waxy | 600-1000 | 1.08-1.2 | 20 |
Safety Shoes Materials Materials preheat
A-6170: preheated at 50-60℃ for 6-8℃ hours
B-8280: preheated at 50-60℃ for 8-12 hours
Shoe Sole Polyurethane Resins
Typical processing parameters & Reaction parameter
| Items | A/B Materials Temperatures(℃) |
Mix ratio A+C/B (By weight)
|
Cream time (s) |
End of Rise Time (s) |
||
| Parameter | 40-45/40-45 | sole | mid-sole | sole | mid-sole | 40-50 |
| 100/69-71 | 100/77-79 | 6-8 | 6-7 | |||
| Items |
Free Rise Foam Density (g/cm³) |
Mold Temperature (℃) |
Demold Time (min) |
|
| parameter | sole | mid-sole | 45-55 | 3-5 |
| 0.60-1.0 | 0.23-0.27 | |||
The adding content of C-2 should be 300g±10g/18kg
The adding content of water and hardener should be changed according to the reality
Sole: H2O 0-30g/18kg Hardener 0-400g/18kg
Mid-sole: H2O 50-55g/18kg Hardener 0-600g/18kg
Physical properties
| Items |
Molded Density (g/cm³)
|
Hardness (Shore A)
|
Tensile strength (Mpa)
|
Elongation (%)
|
||||
|
Physical properties
|
sole | mid-sole | sole | mid-sole | sole | mid-sole | sole | mid-sole |
| 0.9-1.1 | 0.45-0.55 | 62-72 | 45-55 | 8.0-11.0 | 3.9-7.9 | 550-750 | 520-690 | |
| Items |
Tear strength (kN/m) |
Flexing resistance |
DIN abrasion (mm³) |
Peel strength between sole and mid-sole (kN/m) |
||
| Physical properties | sole | mid-sole | 100000 times no crack | sole | mid-sole | ≥3.5 |
| 25-40 | 16-27 | 60-100 | ---- | |||
Demold time may be prolonged with the increse of sole thickness
These physical data are acquired by testing a sample of 6mm thick
Data listed above are just for reference.The data are subjected to practical production.If other requests for physical properties,please contact us.