Polyurethane System For Safety Shoe
- Min. Order:
- 1000 Ton
- Min. Order:
- 1000 Ton
- Transportation:
- Ocean
- Port:
- Shanghai
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | China |
|---|---|
| Productivity: | 250000 tons/year |
| Supply Ability: | 250000 tons/year |
| Payment Type: | L/C,T/T,D/P |
| Incoterm: | FOB,CFR,CIF |
| HS Code: | 39095000 |
| Transportation: | Ocean |
| Port: | Shanghai |
Polyurethane System For Safety Shoes Materials
POLYESTER -POLYURETHANE FOOTWEAR SYSTEM
Material name: XC-6170/XC-8280
Characteristic : High strength, good abrasion resistance and skid resistance.(FOR DESMA machine)
Application: Double density safety shoes and casual shoes
Polyester Polyol Isocyanate
|
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
|
XC-6170(POL) |
cream white liquid |
1000~1400 |
1.01~1.02 |
225 |
|
XC- 8280(ISO) |
Yellowish transparent liquid |
600~1000 |
1.08~1.2 |
225 |
Typical processing parameters & Reaction parameter
|
Items |
POL/ISO Materials Temperatures (℃) |
POL/ISO Mix ratio (By weight) |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature (℃) |
Demold Time(min) |
||
|
Parameter |
40~45/35~40 |
outsole |
midsole |
6~8 |
40~50 |
sole |
midsole |
45~55 |
3~5 |
|
100/69~71 |
100/77~79 |
0.47~0.5 |
0.23~0.26 |
||||||
Shoe Sole Polyurethane Resins
Molded shoe sole physical properties
|
Items |
Molded Density (g/cm3) |
Hardness (Shore A ) |
Tensile strength (MPa) |
Elongation (%) |
Tear Strength (kN/m) |
Flexing Resistance |
|||||
|
Physical properties |
outsole |
midsole |
outsole |
midsole |
outsole |
midsole |
outsole |
midsole |
outsole |
midsole |
100,000times no crack |
|
0.9~1.1 |
0.45~0.55 |
65~75 |
40~50 |
9~12 |
5~9 |
600~720 |
550~660 |
29~42 |
24~32 |
||
*Demold time may be prolonged with the increase of sole thickness
*These physical data are acquired by testing a sample of 6mm thick.
*Any questions are welcomed,24h online
-----------------------------------------------------------------------------------------------------------------------------------------------------------------------------