Pu resin for women wedge sandals and out-sole
- Min. Order:
- 1000 Kilogram
- Min. Order:
- 1000 Kilogram
- Transportation:
- Ocean, Land, Air
- Port:
- Shanghai
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | China,Jiangsu |
|---|---|
| Productivity: | 250000 tons/year |
| Supply Ability: | 250000 tons/year |
| Payment Type: | T/T,L/C |
| Incoterm: | FOB,CIF |
| Transportation: | Ocean,Land,Air |
| Port: | Shanghai |
HIGH-HARDNESS POLYESTER
XC-9002F/XC-6230T
Charcteristic:Low density and medium hardness,good flexing resistance
Appliation:Woman wedge sandals and out-sole
Shock Absorption Mat Raw Materials
Typical properties of PU matrix
Materials preheat
Name of products
Appearance
Viscosity(mPa.S/40℃)
Density(g.cm-3/40℃)
Package(kg)
A-9002F
Liquid
1200-1800
1.01-1.02
18
B-6230T
Yellowish tranpsparent liquid or waxy
600-800
1.08-1.2
20
A-9002F:preheated at 50-60℃ for 6-8 hours
B-6230T:preheated at 50-60℃ for 8-10 hours
Pu Hard Materials
Typical processing parameters& Reaction parameter
The adding content of C-2 should be 270g±10g/18kg
Items
A+B Materials Temperatures(℃)
Mix ratio A+C+70gH2O/B(By weight)
Cream Time(s)
End of Rise Time(s)
Free Rise Foam Density(g/cm³)
Mold Temperature(℃)
Demold Time(min)
Parameter
40-45/38-42
100/87-89
6-8
25-30
0.19-0.24
55-65
5-7
The adding content of water and hardener should be changed according to the reality
Physical properties
Rose Flexing -90℃（room temperature）
(40000 times break length 4mm)
Items
Molded Density(g/cm³)
Hardness(Shore C)
Tensile strength(MPa)
Elongation(%)
Tear Strength (kN/m)
DIN abrasion(mm³)
Physical properties
0.38-.048
70-80
4.2-6.9
360-450
18-27
no increase
140-200
Raw Material Polyester Resin
Demold time may be prolonged with the increase of sole thickness.
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference.The detail data are subjected to practical production.If other requests for Physical properties,please contact us.