Polyol and Isocyanate polyurethane resin stone sealant glue for shoe sole
Women's Shoe Sole Product Detail
| Application | shoe sole |
| Keywords | Lady shoe sole |
| A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
| A+C/B Mix ratio (By weight) | 100/100~102 |
| Cream Time (s) | 6~8 |
| End of Rise Time (s) | 30~40 |
| Free Rise Foam Density(g/cm3) | 0.21~0.26 |
| Mold Temperature(℃) | 45~55 |
| Demold Time(min) | Demold Time(min) |
| Molded Density (g/cm3) | 0.35~0.60 |
|
Low Density Shoe System Characteristic |
|
: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
|
Application: Outsole, slippers, wedge shoes |
|||||||
|
Typical properties of PU matrix |
|||||||
|
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
|
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
|
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
|
Raw Material Polyester Resin Materials preheat |
|||||||
|
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
|
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
|
Typical processing parameters & Reaction parameter. |
|||||||
|
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
|
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
|
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
|
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
|
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
|
Physical properties |
|||||||
|
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
|
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
|
|
|||||||
These physical data are acquired by testing a sample of 6mm thick.
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.