POLYETHER(PTMEG) TDI PREPOLYMER For Tyres and Carts Wheel
- Min. Order:
- 1000 Kilogram
- Min. Order:
- 1000 Kilogram
- Transportation:
- Ocean
- Port:
- Shanghai
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | China |
|---|---|
| Productivity: | 250000 tons/year |
| Supply Ability: | 250000 tons/year |
| Payment Type: | L/C,T/T,D/P |
| Incoterm: | FOB,CFR,CIF |
| HS Code: | 39095000 |
| Transportation: | Ocean |
| Port: | Shanghai |
|
POLYETHER(PTMEG) TDI PREPOLYMER XCPU-M135 |
1,This product is a polytetrahydrofuran ether polyol(PTMEG) and toluene diisocyanate (T-100) synthesis of polyether polyurethane prepolymer
2,Features: Water resistance, low temperature resistance, mildew resistance
3,Application: Typical uses of this polymer include forklift truck tyres, rolls, and gears, die pads etc.
4,Product Specifcation
|
Name of products |
Appearances |
Viscosity(mPa.s/85℃) |
NCO% content |
Package(kg) |
|
XCPU-M135 |
solid |
1200-1300 |
3.50-3.70 |
20 / 200 |
5,Mixing and Curing Conditions
|
MOCA Level |
Recommended % Theory |
Prepolymer Temperature |
Curative Temperature |
Pot Life |
Demould Time |
Post Cure Time |
|
% |
% |
℃ |
℃ |
mins |
@ 100°C (hrs) |
@ 100°C (hrs) |
|
10.5 |
95 |
75-85 |
110-120 |
11-12 |
1 |
10 |
6,Processing Procedure:
Prepolymer at 75 ~ 85 ℃ preheating, after vacuum degassing, the melt MOCA good homogeneous mixing, deaeration, pouring, molding, vulcanization molding, stripping, vulcanization.
Cpu For Tyres Wheel
7,Physical Properties
Properties presented below are to be used as a guide and not intended for specification purposes.
Pu Casting Gear Wheel
|
Hardness |
Shore A |
85 |
|
Tensile Strength |
MPa |
27 |
|
100% Modulus |
MPa |
5.4 |
|
300% Modulus |
MPa |
9.6 |
|
Angle Tear Strength, Die C |
kN/m |
65 |
|
Trouser Tear Strength |
kN/m |
21 |
|
Elongation |
% |
550 |
|
Resilience |
% |
61 |
|
DIN Abrasion Resistance 10N |
mm 3 |
39 |
|
Cured Specific Gravity |
g/cm3 |
1.07 |