Cpu For Elastomers
|
POLYETHER PREPOLYMER XCPU-P155 |
1,This product is a polyether polyol and toluene diisocyanate (T-100) synthesis of
polyether polyurethane prepolymer
2,Features: Water resistance, low temperature resistance, mildew resistance
3,Uses:PU plate ,PU bar, Sealing ring, PU rollers and other products
4,Product Specifcation
|
Name of products |
Appearances |
Viscosity(mPa.s/85℃) |
NCO% content |
Package(kg) |
|
XCPU-P155 |
liquid |
250-270 |
5.50-5.70 |
20 / 200 |
5,Mixing and Curing Conditions Prepolymer For Pu Plate
|
MOCA Level |
Recommended % Theory |
Prepolymer Temperature |
Curative Temperature |
Pot Life |
Demould Time |
Post Cure Time |
|
% |
% |
℃ |
℃ |
mins |
@ 100°C (hrs) |
@ 100°C (hrs) |
|
16.6 |
95 |
75-85 |
110-120 |
9-10 |
1 |
10 |
6,Processing Procedure:
Prepolymer at 75 ~ 85 ℃ preheating, after vacuum degassing, the melt MOCA good
homogeneous mixing, deaeration, pouring, molding, vulcanization molding, stripping, vulcanization.
Polyether Polyurethane Prepolymer
7,Physical Properties
Properties presented below are to be used as a guide and not intended for specification purposes.
|
Hardness |
Shore A |
88 |
|
Tensile Strength |
MPa |
32 |
|
100% Modulus |
MPa |
5.5 |
|
300% Modulus |
MPa |
13 |
|
Angle Tear Strength, Die C |
kN/m |
76 |
|
Trouser Tear Strength |
kN/m |
19 |
|
Elongation |
% |
400 |
|
Resilience |
% |
24 |
|
DIN Abrasion Resistance 10N |
mm 3 |
109 |
|
Cured Specific Gravity |
g/cm3 |
1.14 |