Polyether Polyurethane Prepolymer
Product Description
Cpu For Elastomers
|
POLYETHER PREPOLYMER XCPU-P145 |
1,This product is a polyether polyol and toluene diisocyanate (T-100) synthesis of polyether polyurethane prepolymer
2,Features: Water resistance, low temperature resistance, mildew resistance
3,Uses:PU plate ,PU bar, Sealing ring, PU rollers and other products
4,Product Specifcation
|
Name of products |
Appearances |
Viscosity(mPa.s/85℃) |
NCO% content |
Package(kg) |
|
XCPU-P145 |
liquid |
300-330 |
4.50-7.70 |
20 / 200 |
5,Mixing and Curing Conditions
|
MOCA Level |
Recommended % Theory |
Prepolymer Temperature |
Curative Temperature |
Pot Life |
Demould Time |
Post Cure Time |
|
% |
% |
℃ |
℃ |
mins |
@ 100°C (hrs) |
@ 100°C (hrs) |
|
13.5 |
95 |
75-85 |
110-120 |
9-9.5 |
1 |
10 |
6,Processing Procedure:
Prepolymer at 75 ~ 85 ℃ preheating, after vacuum degassing, the melt MOCA good homogeneous mixing, deaeration, pouring, molding, vulcanization molding, stripping, vulcanization.
7,Physical Properties
Properties presented below are to be used as a guide and not intended for specification purposes.
|
Hardness |
Shore A |
82 |
|
Tensile Strength |
MPa |
25 |
|
100% Modulus |
MPa |
5.1 |
|
300% Modulus |
MPa |
9.2 |
|
Angle Tear Strength, Die C |
kN/m |
55 |
|
Trouser Tear Strength |
kN/m |
14 |
|
Elongation |
% |
480 |
|
Resilience |
% |
24 |
|
DIN Abrasion Resistance 10N |
mm 3 |
112 |
|
Cured Specific Gravity |
g/cm3 |
1.12 |
Polyseter Prepolymer For Ring