polyol and isocyanate for insole

Get Latest Price

Delivery Time:: 10 Days

Quantity:

Your message must be between 20 to 2000 characters

Contact Now

Basic Info

Place of Origin:	Jiangsu, China (Mainland)

Product Description

XC-1001A/XC-5301

Application: Insole

Name of products	Appearance	Viscosity (mPa·s/4℃)	Density (g·cm-3/40℃)	Package(kg)
XC-1001A(A)	cream white liquid	500~800	1.01~1.02	18
XC-5301(B)	Yellowish Transparent liquid or waxy	300~600	1.08~1.2	20

XC-1001A:preheated at 50~60℃ for 2~4 hours XC-5301:preheated at 60~70℃ for 10~15 hours

Items

A/B Materials Temperatures

(℃)

A+C/B Mix ratio

(By weight)

Cream Time (s)

End of Rise

Time (s)

Free Rise Foam

Density(g/cm3)

Mold

Temperature(℃)

Demold

Time(min)

Parameter

30~35/35~40

100/45~47

7~9

50~60

0.13~0.16

45~55

3~5

The adding content of C-2 should be 380g±20g/18kg The adding content of water should be 0~90g/18kg according to the reality The adding content of water should be 0~600g/18kg according to the reality

Items

Molded Density (g/cm3)

Hardness

(Shore C )

Tensile strength

(MPa)

Elongation (%)

Tear Strength

(kN/m)

168h, 70℃, 95%r.h. hydrolysis

strength retention(%)

Physical properties

0.25~0.40

28~50

2.0~5.0

300~380

18~26

>90

Demold time may be prolonged with the increase of sole thickness These physical data are acquired by testing a sample of 6mm thick. Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us.

Send your message to this supplier

* From:
* To:

Mr. Javan Liu
* Messages:

Enter between 20 to 4,000 characters.

Related Keywords

polyol and isocyanate , polyol and prepolymer , polyol and mdi