Made In China Foam pu resin for marine fender With High Quality

        POLYETHER -POLYURETHANE TYRE SYSTEM  Material name: XC-1006A/XC-5009 Characteristic: Good hydrolysis resistance and high strength Application: marine fender, shock absorption mat Typical properties of PU matrix  

Name of products	Appearance	Viscosity (mPa·s/40℃)	Density (g·cm-3/40℃)
A-1170	Liquid	400~800	1.01~1.02
B-6001	Yellowish transparent liquid	600~1000	1.08~1.2

    Typical processing parameters & Reaction parameter

Items	A/B Materials Temperatures (℃)	A/B Mix ratio (By weight)	Cream Time (s)	End of Rise  Time (s)	Free Rise Foam  Density(g/cm3)	Mold Temperature (℃)	Demold Time(min)
Parameter	30~35/35~40	100/103~105	8~10	60~70	0.30~0.35	35~45	7~9

  Physical properties 

Items	Molded Density (g/cm3)	Hardness (Shore A )	Tear Strength (kN/m)	Tensile strength (MPa)	Elongation  (%)
Physical  properties	0.50~0.70	70~90	29.5~44.5	8.0~11.0	335~450

     *Demold time may be prolonged with the increase of sole thickness   *These physical data are acquired by testing a sample of 6mm thick.   * Any questions are welcomed,24h online ----------------------------------------------------------------------------------------------------------------------------------------------------------------------------- Angus Yang                        Sales engineer  Polyurethanes-International Trade Dept  XuChuan Chemical (Suzhou) Co., Ltd   Mob:  +86-(0)13776502417  Zip:215434 Tel:    +86-512-53639253      Fax: +86-512-53639252 Http://www.chinaxuchuan.com Add:No.3 XiexinRd,Gangkou Development Zone,Taicang,Jiangsu,China