1. specifications

XC-9080W/XC-6088

Application: lady’s sole, wedge shoes, platform

Name of products	Appearance	Viscosity (mPa·s/40℃)	Density (g·cm-3/40℃)	Package(kg)
XC-9080W(A)	Cream white liquid	1000~1300	1.01~1.02	18
XC-6088(B)	Yellowish transparent liquid or waxy	600~800	1.08~1.2	20

XC-9080W: preheated at 80~100℃ for 6~8 hours XC-6088: preheated at 80~100℃ for 6~8 hours

Items

A/B Materials Temperatures(℃)

A+C/B Mix ratio

(By weight)

Cream Time (s)

End of Rise

Time (s)

Free Rise Foam

Density(g/cm3)

Mold

Temperature(℃)

Demold

Time(min)

Parameter

40~45/38~42

100/105~120

6~8

30~40

0.17~0.21

45~55

3~5

The adding content of C-2 should be 210g±10g/18kg The adding content of water should be 0~90g/18kg according to the reality The adding content of hardener should be 0~1200g/18kg according to the reality

Items

Molded Density (g/cm3)

Hardness

(Shore A )

Tensile strength

(MPa)

Elongation

(%)

Tear Strength

(kN/m)

Williams abrasion

(cc/php)

Physical properties

0.35~0.45

70~90

4~7

200~300

11~20

130~200

Demold time may be prolonged with the increase of sole thickness These physical data are acquired by testing a sample of 6mm thick. Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. 2.Advantages